Alloy30 Stranded Copper Nickel Alloy Wire 7 Ends 0.18mm For Automobile Cables Heating Cables

Shanghai Tankii Alloy Material Co.,Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment

Alloy30 Stranded Copper Nickel Alloy Wire 7 Ends 0.18mm For Automobile Cables Heating Cables

Brand Name : Tankii

Model Number : CuNi2

Certification : ISO9001

Place of Origin : China mainland

MOQ : 10kg per size

Price : Negotiable

Payment Terms : Western Union, L/C, D/A, D/P, T/T

Supply Ability : 1000T per year

Delivery Time : 3-5 days after getting the payment

Packaging Details : Standard export package

Grade : Cuni2

Wire shape : round wire

wire color : Silvery color

Application : Heating element for auto

Density : 8.9

Item : Alloy30 Stranded Wire With 7 Ends 0.18mm Used For Automobile Cables Heating Cables

Contact Now

Alloy30 Stranded Wire With 7 Ends 0.18mm Used For Automobile Cables Heating Cables ​

Product Description

Copper nickel alloy Wire with moderate resistivity and low temperature coefficent of resistance with a flat resistance/temperature curve over a wider range than the "manganins". it also shows better corrosion resistance, and welding performance.


The copper-based low resistance heating alloy is widely used in low-voltage circuit breaker, thermal overload relay, and other low-voltage electrical product. It is one of the key materials of the low-voltage electrical products. The materials produced by our company have the characteristics of good resistance consistency and superior stability. We can supply all kinds of round wire, flat and sheet materials.


Chemical Content, %


Ni

Mn

Fe

Si

Cu

Other

ROHS Directive

Cd

Pb

Hg

Cr
2 - - - Bal - ND ND ND
ND


Mechanical Properties


Max Continuous Service Temp

200ºC

Resisivity at 20ºC

0.05±10%ohm mm2/m

Density

8.9 g/cm3

Melting Point

1090ºC

Tensile Strength,N/mm2 Annealed,Soft
≥220Mpa

Elongation(anneal)

25%(Min)

Elongation(cold rolled)

≥Min)2%(Min)

EMF vs Cu, μV/ºC (0~100ºC)

-12

Micrographic Structure

austenite

Magnetic Property

Non

Type Electrical resistivity
(20degreeΩ
mm²/m)
Temperature coefficient of resistance
(10^6/degree)
Density
g/mm²
Max. temperature
(°c)
Melting point
(°c)
CuNi1 0.03 <1000 8.9 / 1085
CuNi2 0.05 <1200 8.9 200 1090
CuNi6 0.10 <600 8.9 220 1095
CuNi8 0.12 <570 8.9 250 1097
CuNi10 0.15 <500 8.9 250 1100
CuNi14 0.20 <380 8.9 300 1115
CuNi19 0.25 <250 8.9 300 1135
CuNi23 0.30 <160 8.9 300 1150
CuNi30 0.35 <100 8.9 350 1170
CuNi34 0.40 -0 8.9 350 1180
CuNi40 0.48 ±40 8.9 400 1280
CuNi44 0.49 <-6 8.9 400 1280


Our advantages:

a) We can provide high quality material, excellent design, precise manufacturing,complete specifications, considerate and integrity serivices.
b) We can provide all kinds of electric heating alloy material and elements, including customized products.
c) We can provide a complete solution for you.
d) OEM service can be provided.
e) Product selection
f) Process optimization
g) New product development

Product picture:

Alloy30 Stranded Copper Nickel Alloy Wire 7 Ends 0.18mm For Automobile Cables Heating Cables

Package:

Alloy30 Stranded Copper Nickel Alloy Wire 7 Ends 0.18mm For Automobile Cables Heating Cables


Product Tags:

nickel copper alloy

      

copper and nickel alloy

      
 Alloy30 Stranded Copper Nickel Alloy Wire 7 Ends 0.18mm For Automobile Cables Heating Cables Manufactures

Alloy30 Stranded Copper Nickel Alloy Wire 7 Ends 0.18mm For Automobile Cables Heating Cables Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shanghai Tankii Alloy Material Co.,Ltd
*Subject:
*Message:
Characters Remaining: (0/3000)
 

Friendly Links: www.everychina.com

Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

Copyright © 2009 - 2024 entremaqueros.com. All rights reserved.